GH4169(Inconel 718)

GH4169 is a Nb-Mo reinforced nickel-based high-temperature alloy. Its normal working environment is 253-650C. It has good mechanical properties below 650C. Under special circumstances, GH4169 can be used at 800°C for a short period of time. GH4169 is suitable for many high temperature applications, such as gas turbine components

Low MOQ

Provide low minimum order quantity to meet different needs.

OEM & ODM

Provide customized products and design services to meet unique customer needs.

Adequate Stock

Ensure fast order processing and provide reliable and efficient service.

Customer Satisfaction

Provide high quality products with customer satisfaction at the core.

share this product

Table of Contents

GH4169 is a Nb-Mo reinforced nickel-based high-temperature alloy. Its normal working environment is 253-650C. It has good mechanical properties below 650C. Under special circumstances, GH4169 can be used at 800°C for a short period of time. GH4169 is suitable for many high temperature applications, such as gas turbine components.

Physical properties

Size range
Size distribution
Hall flow rate
Bulk density
Tap density
D10(μm) D50(μm) D90(μm)
15-53μm 17-22 32-38 52-58 ≤18s/50g ≥4.20g/cm³ ≥4.80g/cm³

Heat treatment recommendations

980-1060°C/1h/AC+720°C±10°C/8h/F一620C10C/8h/AC

Mechanical behavior

815°C high temperature durability performance
Constant stress (δ/Mpa) Duration(t/h)
Elongation after break(δ5/%)
690 80 5

GH4169

Test temperature Tensile strength (σb/Mpa) Yield strength (σp0.2/Mpa)
Elongation (δ5/%)
25℃ 1270 1030 12
650℃ 1000 860 12

Chemical composition range (wt,-%)

Element C Cr Ni Co Nb Mo
wt% 0.02-0.06 17.00-21.00 50.00-55.00 ≤1.00 4.75-5.50 2.80-3.30
Element Al Ti Fe B Mg Mn
wt% 0.20-0.80 0.65-1.15 Bal ≤0.006 ≤0.010 ≤0.35
Element Si P S Cu O N
wt% ≤0.35 ≤0.015 ≤0.015 ≤0.30 ≤0.020 ≤0.015