CuCrZr 분말

CuCrZr Powder Overview

CuCrZr 분말은 구리(Cu), 크롬(Cr), 지르코늄(Zr)으로 구성된 합금 분말입니다. 이는 높은 강도, 우수한 전도성 및 고온에서의 연화 저항성을 요구하는 고성능 응용 분야에 적합한 고유한 특성 조합을 제공합니다.

Composition of CuCrZr Powder

CuCrZr is a precipitation hardened alloy meaning its high strength comes from coherent precipitates formed in the metal matrix. The composition plays a key role in achieving optimal precipitation hardening response. Here are the typical composition ranges:

요소	구성 범위
구리(Cu)	나머지
크롬(Cr)	0.5 – 1.2 wt%
지르코늄(Zr)	0.03 – 0.3 wt%

• Copper forms the matrix and provides thermal and electrical conductivity.
• Chromium contributes to solid solution strengthening and forms precipitates to impede dislocation motion.
• Zirconium forms coherent precipitates with copper enabling precipitation hardening.

The chromium and zirconium content is optimized to maximize strength through precipitation hardening while still retaining decent conductivity.

Properties of CuCrZr Powder

CuCrZr powder offers an exceptional combination of strength, conductivity and heat resistance owing to its precipitation hardened nature. Here are some key properties:

속성	가치
밀도	8.8 g/cm3
전기 전도성	22 – 48% IACS
열 전도성	200 – 300 W/m-K
융점	1065°C
열팽창 계수	16.5 x 10<sup>-6</sup> /°C
탄성 계수	124 GPa
수율 강도	350 – 650 MPa
신장	8-15%
산화 저항	Good up to 900°C

• It has high strength coming from precipitation hardening while still retaining moderate conductivity. Strength can be tailored via heat treatment.
• Excellent conductivity compared to precipitation hardened stainless steels due to higher copper content in matrix.
• Good heat resistance with strength and conductivity retention up to 400-500°C. Less prone to softening compared to other Cu alloys.
• Resistant to oxidation and corrosion due to the formation of protective Cr2O3 oxide scale.

This unique property profile makes CuCrZr suitable for applications like resistance welding electrodes, thermal management components and high temperature springs.

Applications and Uses of CuCrZr Powder

The balanced properties of CuCrZr powder make it suitable for the following applications:

애플리케이션	Reason for Use
Resistance Welding Electrodes	High strength, good conductivity, resistance to deformation at elevated temperatures
Heat Sinks and Heat Pipes	High thermal conductivity combined with high temperature strength
Electrical Contacts and Connectors	Good conductivity, high strength enables miniaturization
High Temperature Springs	Strength retention at elevated temperatures
Glass Sealing Alloys	Close match of CTE with borosilicate glass

• Resistance welding electrodes – Its excellent conductivity generates less heat while welding allowing faster weld times. High strength resists mushrooming of electrode tips.
• 열 관리 – Used in heat exchangers, heat sinks, heat pipes etc. where high thermal conductivity rapidly dissipates heat while maintaining mechanical integrity.
• 전기 접점 – Can replace beryllium copper contacts in many applications due to superior strength and similar conductivity.
• High temperature springs – Used for springs operating up to 500°C without losing load capacity unlike steel springs.
• Glass-to-metal seals – Its CTE matches borosilicate glass enabling low stress glass sealing applications.

The precipitation hardening ability of CuCrZr allows tailoring strength as per the specific application requirements simply by modifying heat treatment parameters.

CuCrZr Powder Specifications

CuCrZr powder is available in various size ranges, purities and can be customized as per application needs. Here are some common specifications:

사양	세부 정보
크기 범위	10 - 150 미크론
순도	최대 99.9%
탄소 함량	<100 ppm
산소 함량	<500ppm
파티클 모양	구형, 불규칙
겉보기 밀도	Up to 80% of theoretical density
유량	최대 25초/50g

• Powder size directly affects density and surface finish of finished parts. Finer powder produces higher density and better surface finish.
• High purity reduces contamination issues during consolidation and improves final properties.
• Gas atomized powder has smooth spherical morphology ideal for additive manufacturing. Water atomized powder has irregular shape useful for press and sinter applications.
• Apparent density indicates how tightly powder can be packed. Higher densities improve sintering.
• Flow rate affects ease of powder handling and uniform die filling in press and sinter process.

Powder attributes can be customized like particle size distribution, shape, apparent density etc. as per application requirements.

Consolidation Methods for CuCrZr Powder

CuCrZr powder can be consolidated into fully dense components using methods like:

Consolidation Method	세부 정보
적층 제조	Selective laser melting, Electron beam melting
누르고 소결	Followed by infiltration or further heat treatment
열간 등방성 프레스	Full densification of encapsulated powder
압출	Forging of powder blended with lubricants
스파크 플라즈마 소결	Rapid densification using pulsed current

Additive manufacturing methods like selective laser melting and electron beam melting are commonly used to produce complex, net-shape CuCrZr parts with fine microstructure directly from powder.

Press and sinter method is economical for high volume production but involves multiple steps. Final properties depend on sintering temperature, time, atmosphere etc.

Hot isostatic pressing applies high pressure allowing full densification at lower temperatures. It reduces porosity in additively manufactured parts and improves fatigue life.

Extrusion and spark plasma sintering are alternate methods suitable for simpler geometries. The consolidation process influences final microstructure, properties and performance.

Heat Treatment of CuCrZr Alloy

A key benefit of CuCrZr alloy is its precipitation hardening response. Solutionizing and aging heat treatments can significantly alter its strength as per requirements:

열처리	세부 정보
Solution Annealing	850-980°C, water quench. Dissolves precipitates, softens alloy
Aging	350-500°C for 1-4 hours. Controls precipitation and hardening.
스트레스 해소	350°C for 1 hour. Removes residual stresses.

Solution annealing dissolves chromium and zirconium in solid solution followed by rapid quenching to form a supersaturated solid solution. Subsequent aging treatment nucleates fine coherent precipitates resulting in precipitation hardening.

Aging time and temperature directly controls the hardening response. Lower aging temperature and shorter times preserve conductivity. Precipitation hardening can triple the strength compared to solutionized condition.

Stress relieving helps reduce residual stresses from prior cold or hot working to minimize distortion during machining.

Comparison of CuCrZr Powder with Alternatives

CuCrZr competes against alloys like precipitation hardened stainless steels, beryllium copper and nickel silver:

합금	CuCrZr	17-4PH SS	Be-Cu	Ni-Ag
힘	우수	우수	공정	양호
전도성	양호	Poor	우수	양호
작업 효율성	공정	양호	우수	우수
용접성	공정	공정	우수	양호
비용	보통	높음	매우 높음	보통

• 17-4PH stainless has comparable strength but significantly lower conductivity due to higher Cr and Ni content.
• Beryllium copper has excellent conductivity but lower strength levels. Expensive and toxicity issues.
• Nickel silver has good strength but lower operating temperatures. Excellent formability.
• CuCrZr offers the best balance of strength, conductivity, workability and cost for many applications.

For strength plus conductivity combination, CuCrZr provides higher performance and lower cost compared to precipitation hardened stainless steels or beryllium copper alloys.

CuCrZr Powder Suppliers

CuCrZr powder is supplied by specialty metal powder producers. Here are some of the major suppliers:

공급업체	Powder Attributes
샌드빅	Size range 10-150 μm, Apparent density up to 65%, Irregular and spherical powder
호가나스	Size range 45-150 μm, Apparent density up to 80%, Spherical powder, High purity
포메톤	Size range 10-63 μm, Apparent density up to 65%, Spherical and irregular powder
CNPC 파우더	Size range 10-150 μm, Apparent density up to 75%, High purity

Various powder grades are available optimized for additive manufacturing, press and sinter applications, or tailored for specific customer requirements.

Reputable suppliers have extensive quality control in powder production and provide mill certificates with proof of batch composition.

CuCrZr Powder Pricing

As a specialty alloy powder, CuCrZr is more expensive than standard material powders. Here are some typical pricing ranges:

파우더 등급	입자 크기	가격 범위
CuCrZr for AM	15-45 μm	$100-150kg당
CuCrZr for Press & Sinter	45-150 μm	kg당 $50-100
High Purity CuCrZr	10-45 μm	$180-250 per kg

• Fine powder below 45 microns is generally over $100/kg ideal for additive manufacturing.
• Coarser powder 45-150 microns costs $50-100/kg suitable for press and sinter route.
• High purity (>99.9%) powder intended for critical applications commands premium pricing over $180/kg.
• Reducing oxygen and carbon content improves consolidation and final properties.
• Prices vary with quantity, size range, quality level of powder.

Volume discounts from 1 kg to multiple tons may be negotiated with suppliers. High purity powder with controlled particle size distribution attracts higher pricing.

CuCrZr Powder: Health and Safety

Like most metal powders, CuCrZr powder requires careful handling to minimize health and safety risks:

위험	주의 사항	PPE
아이 컨택	Avoid direct contact. Do not rub eyes after exposure. Rinse with water if contacted.	보안경
피부 접촉	Avoid direct contact. Wash affected areas thoroughly with soap and water.	장갑
흡입	Avoid breathing powder dust. Ensure adequate ventilation.	Approved respirators
섭취	Avoid hand to mouth contact. Wash hands after handling.	–
화재	Use dry sand to extinguish metal powder fire. Do not use water.	Fire safety gear

• Wear PPE – goggles, gloves, respirator when handling powder to minimize contact.
• Practice good hygiene after working with powder.
• Prevent accumulation of powder dust on surfaces.
• Store sealed containers in cool, dry area away from sources of ignition.

Refer to SDS for complete safety information. Get medical assistance if exposure causes irritation. Having proper safety protocols minimizes risks when handling CuCrZr powder.

Inspection and Testing of CuCrZr Powder

To ensure high quality and consistency, CuCrZr powder should be inspected and tested for:

매개변수	방법	사양
화학 성분	XRF, wet chemistry	Conformance to specified Cu, Cr and Zr content
입자 크기 분포	레이저 회절, 체질	Median size, D10, D90 within specified range
분말 형태	SEM 이미징	Spherical shape, minimal satellites for AM powder
겉보기 밀도	홀 유량계	As specified for application
유량	홀 유량계	As specified for application
불순물	ICP, LECO analysis	Low oxygen and nitrogen content

Proper in-process QC testing and final inspection ensures the powder meets the chemical, physical and morphological attributes required for the intended application. Routine testing should be implemented by both powder producer and user.

자주 묻는 질문

Q. What is CuCrZr alloy used for?

A. CuCrZr is used in applications requiring high strength combined with good electrical and thermal conductivity like resistance welding electrodes, heat sinks, and high temperature springs.

Q. How is CuCrZr powder made?

A. CuCrZr is produced via gas atomization or water atomization of the molten alloy to create fine spherical or irregular powder particles optimally sized for AM or press and sinter use.

Q. What affects the properties of CuCrZr parts?

A. Properties depend on composition, powder quality, consolidation method and parameters, heat treatment, and microstructure. The precipitation hardening ability of CuCrZr also allows customization of strength.

Q. What is the difference between gas atomized and water atomized CuCrZr powder?

A. Gas atomized powder has a spherical morphology ideal for AM processing whereas water atomized powder has an irregular shape suitable for press and sinter application.

Q. Does CuCrZr alloy need heat treatment?

A. Yes, solution annealing and aging heat treatments allow optimizing the strength and conductivity by controlling precipitation in the alloy microstructure.

Q. What is the typical price for CuCrZr powder?

A. CuCrZr powder ranges from $50/kg for press and sinter grade to $250/kg for high purity AM grade powder. Finer size fractions and higher purity increase cost.